Professional refractory products manufacturer from China since 1978, deals on exploration, whose products have been exported to more than 20 countries. Product portfolio covers shaped and unshaped products, such as fire brick, impact plate, ladle and tundish nozzle, calcium silicate board and pipe, ceramic fiber, slide gate, repair, construction and casting mortar and mixes, etc.Unknownnoreply@blogger.comBlogger195125tag:blogger.com,1999:blog-3569575769022435283.post-15375146842680150142023-04-10T13:58:00.003+08:002023-04-10T13:58:23.258+08:00Refractory Material, Fire Bricks, Refractory Manufacturer, China Refractory - CX Refractories<a href="https://www.chinafirebrick.com/index.html">Refractory Material, Fire Bricks, Refractory Manufacturer, China Refractory - CX Refractories</a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-85017294442960789872023-03-31T15:12:00.002+08:002023-03-31T15:13:33.814+08:00Slide Gate Plate, Ladle slide gate plate<a href="http://www.cxfirebrick.com/en/product/slide-gate-plate.html">Slide Gate Plate, Ladle slide gate plate</a><div><br /></div><div><div><b><a href="http://www.cxfirebrick.com/en/product/slide-gate-plate.html" target="_blank">Slide Gate Plate</a></b></div><div><br /></div><div>Ladle slide gate plate is an essential component in the steelmaking process. It is used to control the flow of molten steel from the ladle to the tundish in the continuous casting process. The slide gate plate is a refractory material that is designed to withstand high temperatures and mechanical stress.</div><div><br /></div><div>Source:</div><div><b><i><a href="http://www.cxfirebrick.com/en/product/slide-gate-plate.html">http://www.cxfirebrick.com/en/product/slide-gate-plate.html</a></i></b></div><div>Email: info@cxfirebrick.com </div></div><div class="separator" style="clear: both; text-align: center;"><a href="http://www.cxfirebrick.com/Uploads/64117e4eb0e85.jpg" style="margin-left: 1em; margin-right: 1em;"></a></div><br /><div><br /></div><a href="http://www.cxfirebrick.com/en/product/slide-gate-plate.html" target="_blank"><img border="0" data-original-height="500" data-original-width="500" height="403" src="http://www.cxfirebrick.com/Uploads/64117e4eb0e85.jpg" width="403" /></a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-23123419437264266752022-02-21T17:07:00.000+08:002022-02-21T17:07:07.569+08:00Monoblock Stopper, Stopper Rods - Changxing Refractory<a href="https://www.yilongrefractory.com/AllProductOneServlet?id1=4&id=57">Monoblock Stopper, Stopper Rods - Changxing Refractory</a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-64757859240352580992022-02-18T17:01:00.003+08:002022-02-18T17:01:16.247+08:00Refractory Materials Supplier, Refractory Products, Magnesia Refractory Material, Furnace Refractory - CX Refractories<a href="http://www.cxfirebrick.com/en/product.html">Refractory Materials Supplier, Refractory Products, Magnesia Refractory Material, Furnace Refractory - CX Refractories</a><div><br /></div><div><div>Refractory Materials Supplier, Refractory Products, Furnace Refractory</div><div><b><i><a href="http://www.cxfirebrick.com/en/product.html">http://www.cxfirebrick.com/en/product.html</a></i></b></div></div>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-63089759518701860072022-02-14T17:17:00.001+08:002022-02-14T17:17:20.498+08:00Refractory Suppliers, Refractory Material, Refractory Fire Brick | CX Refractory<a href="http://www.cxfirebrick.com/">Refractory Suppliers, Refractory Material, Refractory Fire Brick | CX Refractory</a><div><br /></div><div><a href="http://www.cxfirebrick.com/"><b><i>http://www.cxfirebrick.com/</i></b></a></div>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-26042693128054235822021-10-14T16:54:00.002+08:002021-10-14T16:54:20.504+08:00Company News | Xinmi Changxing Refractory Co.,Ltd<a href="https://www.chinafirebrick.com/company_news.html">Company News | Xinmi Changxing Refractory Co.,Ltd</a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-82810008138026761522021-09-29T16:23:00.002+08:002021-09-29T16:23:22.553+08:00Refractory China, Refractories, Refractory Supplier, Refractory Materials - Changxing Refractory<a href="https://www.yilongrefractory.com/">Refractory China, Refractories, Refractory Supplier, Refractory Materials - Changxing Refractory</a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-71763671684448764842019-07-16T11:01:00.000+08:002019-07-16T11:01:06.331+08:00How to do lining construction1.Lift the installed pneumatic vibrator into the forma, put it in the bottom, and then raise it by 50mm. Adjust the distance between the hammer head and the forma. With 30mm as the standard, ensure that the hammer head can effectively contact the inner lining of forma.<br />
<br />
2.Turn on the gas valve for 30 seconds at low speed, then vibrate at full speed, and vibrate for 5 to 8 minutes for each 100mm increase until 300mm below the top of the furnace.<br />
<br />
3. Furnace Heating Technique of Former Patching Lining<br />
3a) Fully fill small and dense scrap materials into the furnace, and heat up at 100-200 celsius degree per hour.<br />
3b) During melting, raise powers slowly to ensure crucible not break until it is full.<br />
3c) Keep heat preservation for one hour at 1680-1700 celsius degree, detecting temperature once per 20 minutes.<br />
3d) After sintering finished inside furnace, it can start to work.<br />
<br />
Article source:<br />
http://www.yilongrefractory.com/news/How%20to%20do%20lining%20construction.html<br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com1tag:blogger.com,1999:blog-3569575769022435283.post-60557589534494319372019-06-14T14:50:00.000+08:002019-06-14T14:50:03.331+08:00Application of Ladle CastablesApplication of Ladle Castables<br />
<br />
<table align="center" cellpadding="0" cellspacing="0" class="tr-caption-container" style="margin-left: auto; margin-right: auto; text-align: center;"><tbody>
<tr><td style="text-align: center;"><span style="margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=24" target="_blank"><img border="0" data-original-height="120" data-original-width="120" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEh3KGCxwkioKdNUJjGeI6Hw9q_zC0y9l9RpDnDZj_ooNRj-yd_ICrJxy3pkBaw6sT4ACqeAzuXVNW4UnK05i8VldhZN_OGM4BFMta5dUxcC4HPWOIBbbai9ByouBZ3TSKWHFXaVPYez_4em/s1600/%25E6%25B5%2587%25E6%25B3%25A8%25E6%2596%25994.jpg" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=24" target="_blank">Ladle Castables</a></td></tr>
</tbody></table>
Because the water content of the whole<b><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=24" target="_blank"> ladle castable</a></b> is large, and the material structure is dense, the water is not easy to be discharged. Therefore, in the ladle baking process, the small heat is long, gradually warming up, preventing rapid heating, and the principle of roasting the fire is strictly prohibited, otherwise the ladle appears. It collapsed and peeled off. Bake with a baking machine and bake in a 72-hour system. The specific distribution is as follows:<br />
<br />
Firstly, small fire stage: no less than 3 shifts, 24 hours (only 1/2 gas, no cover);<br />
Secondly, medium fire stage: no less than 3 shifts, 24 hours (only 1/3 gas is added, plus a little wind, stamped);<br />
At last, fire stage: no less than 3 shifts, 24 hours (open gas, add foot, cover)<br />
<br />
Article source:<br />
<b><a href="http://www.yilongrefractory.com/news/Application%20of%20ladle%20castables.html">http://www.yilongrefractory.com/news/Application%20of%20ladle%20castables.html</a></b><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com1tag:blogger.com,1999:blog-3569575769022435283.post-11514885942954557952019-02-15T14:00:00.001+08:002019-02-15T14:00:25.180+08:00Changxing Refractory,Refractory Brick,Castable,Ladle Nozzle,Calcium Silicate,Silicon Carbide: Advantages of covering agent<a href="https://yilongrefractory.blogspot.com/2019/02/advantages-of-covering-agent.html?spref=bl">Changxing Refractory,Refractory Brick,Castable,Ladle Nozzle,Calcium Silicate,Silicon Carbide: Advantages of covering agent</a>: covering agent 1, Insulation covering agent is made of low thermal conductivity material composition, such as: expanded perlite, expand...cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-81545326211683293522019-02-15T13:17:00.001+08:002019-02-15T13:17:06.873+08:00Advantages of covering agent<table align="center" cellpadding="0" cellspacing="0" class="tr-caption-container" style="margin-left: auto; margin-right: auto; text-align: center;"><tbody>
<tr><td style="text-align: center;"><span style="margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/news/Advantages%20of%20covering%20agent.html" target="_blank"><img alt="covering agent" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEhoZAN1X06nHfDrMUJx-II5Tyr-a0AnjSZqrqXNU80GDc58jMEehPgbnOrmC5pKEaCqZbSRvOptom4b4jUhoYsc_ODVzEZWbuvlcAaQp3h443PcHjChXnb6t1zCpcjzSHJaIYOwXlKS8AYo/s320/covering+agent+1.jpg" title="covering agent" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/news/Advantages%20of%20covering%20agent.html" target="_blank">covering agent</a></td></tr>
</tbody></table>
1, Insulation <b><i><a href="http://www.yilongrefractory.com/news/Advantages%20of%20covering%20agent.html">covering agent</a></i></b> is made of low thermal conductivity material composition, such as: expanded perlite, expanded graphite.<br />
<br />
2.In addition to the low thermal conductivity material, by adding a certain percentage of the heating material, and under the heat of the metal liquid, the oxidant provides oxygen to oxidize the reducing agent and prolong the solidification time of the metal liquid in the riser.<br />
<br />
3.In the case of different insulation covering agent, the mouth shrinks into a "dish-shaped flat or hemispherical bottom, which is shaped like a U-shaped throat.<br />
<br />
Article source:<br />
http://www.yilongrefractory.com/news/Advantages%20of%20covering%20agent.html<br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-43564704344244289592017-12-11T14:50:00.001+08:002017-12-11T14:50:18.374+08:00Ladle with refractory materials are used<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="refractory materials" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEg-Olg2njLSG68hu3S1nZmG4bGrR2ZRx7D0U6ffUaHYvsUFLok8gcn50ZODaIg2tSY1fWN_lbIXUSlGlvBoVZGypBoibYNIO49GAn-2ZDgeJuWVXvx7sZlrRLNk3c22KEbRqXlC-vWM8Vdp/s320/1.+Magnesia+Carbon+Brick.jpg" title="refractory materials" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/">refractory materials</a></td></tr>
</tbody></table>
Common types of ladle refractories:<br />
(1) Clay <b><a href="http://www.yilongrefractory.com/ProductServlet?id=1">refractory brick</a></b>, clay brick A12O3 content is generally between 30% -50%, the price is low. Mainly used for ladle permanent layer and ladle bottom.<br />
(2) <b><a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=85">high alumina brick</a></b>. Brick A12O3 content of 50% -80%, mainly for the working layer ladle.<br />
(3) wax stone brick. The <b><i><a href="http://www.yilongrefractory.com/">refractory supplier</a></i></b> brick is characterized by high SiO2 content. Generally more than 80%, anti-erosion than the clay brick and the integrity of the good, and not hanging residue. Commonly used in the ladle wall and package at the end.<br />
(4) Zircon brick. The brick is mainly used for ladle slag line parts. Brick ZrO2 content is generally between 60% -65%.<br />
(5) <b><a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=1">Magnesia carbon bricks</a></b>. The brick is mainly used for ladle slag line parts, especially for multi-furnace continuous casting occasions. Brick MgO content is generally about 76%, carbon content of 15% -20%. It is characterized by small erosion of slag, erosion resistance, good resistance to spalling.<br />
(6) aluminum-magnesium castables. The castable is mainly used for the steel body, and is characterized in that, under the action of molten steel, MgO and A12O3 in the castable react with each other to form aluminum oval spinel, thereby improving the thermal shock resistance of the lining.<br />
(7) aluminum-magnesium carbon brick. This brick is developed on the basis of aluminum-magnesium castable ladle lining, long service life.<br />
(8) Do not burn brick. At present, the materials used in ladle firing bricks can be made into corresponding unburned brick. Its characteristics are relatively simple production process, the price is lower. Brick itself has a certain mechanical strength and erosion resistance, easy construction masonry.<br />
If the ladle itself is also used for refining, you can also choose MgO-Cr2O3-A10O3 series and <b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=1">magnesia carbon brick</a></i></b> refractory, are: magnesia-chrome brick, magnesia-chrome-aluminum brick, dolomite brick.<br />
In the content of ink material used for ladle lining brick, it is best to apply a layer of anti-oxidation coating on its surface to prevent burning in the package, the lining surface oxidation loose, affecting its service life.<br />
<br />
More refractory:<br />
<b><a href="http://www.yilongrefractory.com/">http://www.yilongrefractory.com/</a></b><br />
E-mail: sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com1tag:blogger.com,1999:blog-3569575769022435283.post-74653199995890849522017-12-11T14:39:00.001+08:002017-12-11T14:39:15.561+08:00Refractory materials for glass furnaces<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="Refractory materials" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEgEZlVbxo2D6Njbr5EpoQBWO-Qjfjs_5ir6-qxJlpbGPLMdpYjdtwRNmK2E6GI-EWe56TyyXgL-GD8HpSy_OtLKT0AYVIcjkqWgSNTpdbklbcOUvL0FcJDJ9uwii77bSRvBOLmmC-BhjmA1/s320/19.+Acid+Proof+Brick.jpg" title="Refractory materials" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/">Refractory materials</a></td></tr>
</tbody></table>
There are three key drivers behind the evolution of refractories: maintaining improved glass quality; economic requirements on glass kilns to make kilns run longer and impact after pure oxygen combustion systems.<br />
The word "current" can be read in months or even weeks as the computer industry in the electronics industry changes. When it comes to the development and application of <a href="http://www.yilongrefractory.com/"><b>refractories</b></a> in the glass industry, it can easily be read as five or ten years. Based on this notion of time, we will recall that there has been a change in the discussion of the "current" area (more conservatively) in the latter area.<br />
There are three major driving forces behind the development of <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory materials</a></i></b>. The first glass manufacturer typically needs to improve glass quality in order to maintain it at least. The second glass kiln economy required a longer kiln operation cycle and a third pure oxygen combustion system with impact. These three requirements usually determine the choice of improved refractories when repairing the kiln. These impetuses have also prompted the glass manufacturer to use the furnace with improved fire-resistant products for maintenance and repair, as well as the introduction of new technologies for a wide range of maintenance runs.<br />
Melting-cast alumina bricks have been melting pool top this part of the establishment of its application, the main melting high-quality glass pure oxygen combustion furnace was applied. Prior to the advent of pure oxygen combustion technology, only beta alumina bricks were used to melt pool superstructure and no melt cast alumina bricks were used on top of the melting pool. Today, both β-alumina and α-β alumina melt-cast products are used to produce color TV (screen cone), float glass and borosilicate glass pure oxygen combustion furnace some or all of the roof. Melt-cast AZS bricks can typically be used at 1600 ° C or 1650 ° C (depending on the glazing), while furnace tops with fused alumina are successfully operated at 1700 ° C. This gives glass manufacturers greater flexibility when creating refractory glass.<br />
For many years, melt-cast AZS roofs have successfully undergone a cooling and reheating test to enable them to use multiple operating cycles. There is now a bit of experience in the successful implementation of top cooling and reheating of fused-alumina roofing, demonstrating an economically viable life when they use two or more cycles of operation. The results of fused alumina furnace roof observation (thermal observation and shutdown) show that these materials are both chemically and mechanically stable. This was the earliest observation of this type of masonry study since there was neither a fused alumina reference nor the empirical basis of its roof application.<br />
High-chromium <b><i>refractory products</i></b> used to be mainly used to enhance the glass furnace, and a small amount used in insulation glass pool furnace. High chrome bricks are increasingly being used by some soda lime glass furnaces. Its main use has not only been limited to all or part of the flow hole, but also for the end wall and to a limited extent for the filler brick. For high chrome brick components, they are potentially dangerously colored, so that high-chromium products are often not compatible with very "white" glass. In the initial period this product was mainly used for colored glass, but high chromium products have also been successfully used in transparent container glass furnaces. The use of high-chromium glass furnaces depends largely on the design of the liquid hole, the cooling of the liquid hole, the daily production of the furnace, and the operation of the furnace. A glass manufacturer may use high-chrome bricks for the entire cover plus the melting tank end wall. High Chromite brickwork liquid caves offer the potential to increase kiln life because this material provides at least twice as much resistance to most glass as molten AZS bricks. However, some design parameters differ from those of fused AZS bricks and need to be discussed with the supplier.<br />
<br />
More refractory:<br />
<b><a href="http://www.yilongrefractory.com/">http://www.yilongrefractory.com/</a></b><br />
E-mail: sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-76100721913690125882017-11-28T16:19:00.001+08:002017-11-28T17:21:11.028+08:00Residual Heat Utilization of Refractory Gas Burning Kiln<table align="center" cellpadding="0" cellspacing="0" class="tr-caption-container" style="margin-left: auto; margin-right: auto; text-align: center;"><tbody>
<tr><td style="text-align: center;"><span style="margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20"><img alt="Refractory" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEjH0RWA_1o2DuAW7c9apNAnYdsz0aHhAEXGRa0MXCdhbFkc7ijBTE7yrrr9nG0oBCgIYnxSucGHr3sg-CMiheig5cNGMBqI6-unhhln9AF1p80XoYr0J0g-UCjaIuGGdHOaIbpfxaXk5FN9/s320/High+Strength+Ramming+Mix+for+Trough.jpg" title="Refractory" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">Refractory</a></td></tr>
</tbody></table>
With the gradual implementation of the national environmental protection policy, the original domestic coal-fired kiln in the <b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory industry</a></b> is about to end its historical mission and replace it with clean natural gas, liquefied gas, light diesel oil, city gas and producer gas as the main New energy kiln. However, China is a large coal producing country, and <b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory material</a></b> are also large energy-hungry households. Some medium-to-low-grade refractories and large-volume refractories are still controlled by the furnace hot gas to ensure fuel supply and production cost control . As a result, the <b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory industry</a></b> has also developed a hot gas tunnel kiln, hot gas intermittent plutonium kiln group, hot gas intermittent shuttle kiln group.<br />
Due to the different kiln body structure and thermal engineering process, intermittent kiln produces 5 times more flue gas than continuous kiln production. In general, the higher the gas temperature, the greater the proportion of heat loss. If the gas temperature is 1093 ℃, the heat loss reaches 55%; when the gas temperature is 1427 ℃, the heat loss reaches 70%. For the firing of <b><a href="http://www.yilongrefractory.com/">refractory</a></b> hot gas intermittent inverted kiln, according to the relevant experimental data show that: flue gas away from the kiln away from the heat about the furnace total heat expenditure of 35% to 40% in the absence of any heat recovery In the case of the measure, the heat balance calculation results, the thermal efficiency is only 10% ~ 15%. This is a big heat loss. Therefore, the use of flue gas heat is a very important energy recovery.<br />
Set the heat exchanger in the flue is an important means of waste heat recovery. The hot air obtained after the heat exchange can be directly sent to the burner for combustion air, or the hot air can be diluted to the drying medium of the product embryo drying kiln or used to make the thermal efficiency of the kiln reach 30% or higher.<br />
When the firing system uses a heat exchanger to preheat the air and use this hot air to make the combustion-supporting combustion air, the thermal efficiency of the kiln can be improved, the fuel consumption can be reduced, and the energy-saving effect can be achieved. And in the organization of high temperature combustion flame temperature can increase, increase heating efficiency, shorten the heating time (firing cycle). And because the hot air volume expansion, resulting in the burner orifice flow rate increases, accelerating the kiln gas circulation, contribute to the kiln temperature uniformity. The data show that: when the preheated air temperature reaches 220 ~ 250 ℃, can reduce fuel consumption by 6% to 8%. At the same time different combustion temperature, the impact on the flame temperature is very large. Even when the gas is not preheated, the combustion temperature of the gas increases significantly as the preheating temperature of the combustion air increases. This not only can solve the problem of low firing temperature, but also plays an important role in saving energy and reducing consumption.<br />
In intermittent kiln production, because the fuel is changed with the heating stage, the amount of flue gas generated by the fuel also changes. In the event of a large fire, since the amount of fuel per unit time increases, the flue gas and temperature also inevitably increase. Preheat air combustion just to meet the requirements of combustion. Metal pipe heat exchangers are commonly used in production. Due to the limitations of high temperature oxidation and mechanical properties, the maximum service temperature is generally limited to below 500 ° C because of their low life (about 0.5 years). Metal pipe aluminum treatment, its service life is only about a year. The use of heat-resistant stainless steel or heat-resistant cast iron, the maximum temperature is generally limited to below 900 ℃. However, due to its high price, the use of units unbearable. 1. Because the fuel is the producer gas, the chimney bricks will not block. Life can be more than 10 years. Designed to ensure that the heat transfer efficiency, heat transfer area as large as possible (such as a group of 4 × 200m3 Square inverted hearth heat exchange area of ??about 230m2), although the volume is large, but the site conditions permit a one-time investment in the province, the flue System resistance is generally about 147 ~ 196Pa, chimney can be selected according to the height (usually about 50m).<br />
<br />
The use of heat exchanger temperature is a very important factor in heat recovery. If the flue gas temperature is 1315 ℃, the use of thermal efficiency of 60% ceramic heat exchanger can save about 48% of fuel, if the use of thermal efficiency of 60% metal heat exchanger, you must first add cold air flue gas temperature dropped to 815 ℃ below, so that only 24% of fuel savings. Table 1 shows the effect of blending cold air on fuel economy.<br />
<br />
In order to play the respective advantages of ceramic and metal heat exchangers, the two are used in tandem, known as a hybrid heat exchanger. First high-temperature flue gas into the ceramic heat exchanger, flue gas temperature dropped to below 815 ℃, and then into the metal heat exchanger. The flow of cold air is first into the metal heat exchanger, the heated air and then into the ceramic heat exchanger for further heating, the final preheated air temperature up to 1093 ℃.<br />
<br />
More refractory:<br />
<b><a href="http://www.yilongrefractory.com/">http://www.yilongrefractory.com/</a></b><br />
E-mail: sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-1531646997362847662017-11-28T16:14:00.000+08:002017-11-28T16:14:12.867+08:00Application of Dry Sludge in Refractory for Blast Furnace<table align="center" cellpadding="0" cellspacing="0" class="tr-caption-container" style="margin-left: auto; margin-right: auto; text-align: center;"><tbody>
<tr><td style="text-align: center;"><span style="margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/news/How%20to%20Choose%20Refractory%20Bricks%20Used%20for%20Different%20Parts%20of%20Blast%20Furnace.html"><img alt="blast furnace refractory" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEhQbIRBANs0BFjB4YWzf2LAUDo6HRKjgd3DTJVIbVgpoBm5ZETneQ3jKKamSBQn8vBoViCk3Kx6yM8O6ARiDRJPBf9jUgz17UbA3guGqd5DT-uUn8kCn-neO7bqS4I9yYEdIwtWYiIb8zO-/s320/31.+Monolithic+Refractories+For+Iron+Trough+Of+Blast+Furnace.jpg" title="blast furnace refractory" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/news/How%20to%20Choose%20Refractory%20Bricks%20Used%20for%20Different%20Parts%20of%20Blast%20Furnace.html">blast furnace refractory</a></td></tr>
</tbody></table>
<b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=81">Blast furnace refractories</a></i></b> are often used stemming, commonly used is a water cannabis mud, but when the steel production is high, this iron mouth stem mud is more susceptible to mechanical scouring and chemical erosion of slag iron, resulting in blast furnace slag Not a net, not only affect the smooth and high yield blast furnace, but also prone to iron in the <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1">refractory brick</a></i></b> process of iron off, leading to runway accidents caused by heavy run. At the same time as Tietou tide, prone to playing Tietou "rocket" burns and other accidents.<br />
The main production of anhydrous stemming ingredients ratio (%): Brown Iron Jade 15-24, 6-15 silicon carbide, coke 20, lime 12-16, tar 18-20. The gun mud compressive strength of 20Mpa, open the mouth opening in the <b><i><a href="http://www.yilongrefractory.com/news/How%20to%20Choose%20Refractory%20Bricks%20Used%20for%20Different%20Parts%20of%20Blast%20Furnace.html">blast furnace refractory</a></i></b> openings easy, and anti-erosion performance is better.<br />
The key component of lime mud is too large, will cause mud shrinkage is too large, resulting in cracks, too small, affect the mud plasticity, in the amount of stemming on the basis of 12%, and gradually found in the burn line changes Is +0.3%, the best performance, high plasticity at the moment, when there is good micro-expansion at high temperature tapping, no cracks, effective from the no swelling, cracks caused by channeling iron, , The risk of burned stave in severe cases.<br />
Key components of low, medium temperature sintering agent added in a large amount, will have an impact on the stability of the iron, sintering agent added to the stemming at low temperature to generate low-melt, so anti-erosion ability of stemming deteriorated, splashing spatter . Found that when the ratio of 2.5%, when dealing with the iron mouth, than the water cannons save 25min time, and does not affect the trenches processing, tapping, the iron flow stability.<br />
The above anhydrous mud in the domestic water heaters No. 1 and No. 2 blast furnace used, compared with the same period of water mud, blast furnace technical indicators are as follows: Tiekou pass rate increased by 2%, the punctuality rate rose 6.6%, iron content Poor pass rate rose 8%, iron mouth tapping wind rate decreased 96%, increase once a day tapping, blast furnace operation safety factor has also been improved. The development and application of this anhydrous stem mud has been extremely successful, contributing to the steady and high yield of refractories for blast furnaces.<br />
<br />
Recent article:<br />
<b><a href="http://www.yilongrefractory.com/news/How%20to%20Choose%20Refractory%20Bricks%20Used%20for%20Different%20Parts%20of%20Blast%20Furnace.html">How to Choose Refractory Bricks Used for Different Parts of Blast Furnace</a></b><br />
E-mail: sales8@chinaelong.com<br />
<div>
<br /></div>
cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-645756717911914712017-11-23T15:47:00.000+08:002017-11-23T15:47:39.339+08:00Analysis of the reasons of damaged blast furnace lining fire brick<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=81" style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><img alt="blast furnace refractory lining material" border="0" data-original-height="551" data-original-width="379" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEiVkoGFGXIsppWbJYtExjzbatxCbyTsgV67SMad5RS529jOSGNnoDeXGanOdVm4DB7S9RMxUcmQiyF-DW_zi5_clc2lCQ6yh1-7kzvc02M7h3LCesNFFZkfilpxA90TABaKNWaGGtIS4-nL/s320/Blast-Furnace--.jpg" title="blast furnace refractory lining material" width="220" /></a></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=81">blast furnace refractory lining material</a></td></tr>
</tbody></table>
1.Temperature.<br />
<br />
The damaged performance of high temperature to fire brick:<br />
(1)Erosion. When the edge air develops excessively, but the factory uses poor quality <b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory material</a></b> which has lower refractoriness under load, if the high temperature is over than allowable temperature, the <b><a href="http://www.yilongrefractory.com/ProductServlet?id=1">fire lining brick</a></b> will be eroded.<br />
(2)Heat stress.<br />
(3)Thermal shock. Thermal shock is a phenomenon when the fire brick meet the unsteady thermal stress and then become damaged.Cracks will occur in the <b><a href="http://www.yilongrefractory.com/ProductServlet?id=1">refractory bricks</a></b> and eventually broken.<br />
<br />
2.Mechanical erosion and abrasion<br />
<br />
3.Chemical attack<br />
<br />
4.One of the important factors of <em><strong><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" target="_blank">firebrick refractory sale</a></strong></em> lining damage is unreasonable design, construct and furnace structure. Poor quality refractory and furance construction create the condition for the first kind of destructive factors.<br />
<br />
Article source:<br />
<b><i><a href="http://www.yilongrefractory.com/news/Analysis%20of%20the%20reasons%20of%20damaged%20blast%20furnace%20lining%20fire%20brick.html">http://www.yilongrefractory.com/news/Analysis%20of%20the%20reasons%20of%20damaged%20blast%20furnace%20lining%20fire%20brick.html</a></i></b><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-37217811808850064072017-11-23T15:10:00.001+08:002017-11-23T15:58:26.674+08:00Factors affecting service life of converter<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="converter refractory" border="0" data-original-height="1600" data-original-width="1133" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEhpzwfTDaFdkXPzlWLTlxWHjUPD5DRQLQ5XnelsOsC1sgLnegePeSC7sESqBqk-7ththJvSWV9WEVYt3vuxvipZ8E5TNWO_Z3iqGmGFIhdZPXyREdF5LjA9-G4Nxp5tIxvoiseln4Tgzsca/s320/converter----shuiyin.jpg" title="converter refractory" width="226" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/">converter refractory</a></td></tr>
</tbody></table>
Factors that affect converter life:<br />
<br />
1. Composition of slag. For every 1% increase in iron oxide, the service life of the lining is reduced by 18-20 times; the higher the MgO content in the slag, the lower the erosion of the lining. At present, the iron oxide content of slag is 18-24%.<br />
<br />
2. Tapping temperature. The higher the tapping temperature, the shorter the service life. Therefore, the tapping temperature <em><strong><a href="http://www.yilongrefractory.com/news/Basic%20properties%20of%20refractory%20material%20for%20steel%20making.html" target="_blank">refractory material properties</a> </strong></em>of the converter should be properly controlled.<br />
<br />
3. Smelting time. Long smelting time, will speed the erosion of the lining up.<br />
<br />
4. Lining structure. As the various parts of the converter are in different damage conditions, so it should adopt the integrated masonry method.<br />
<br />
5. Furnace maintenance. For back and forth, regularly repair with hot self-flow repair materials.<br />
<br />
6. Influence of converter blowing. Nitrogen gas, carbon dioxide, argon or oxygen are blown into the furnace through the purging plug placed at the bottom of the converter to enhance the mixing of the molten pool, thus shortening the steel making time, improving the quality of molten steel and reducing the cost of steel making. But the blown also speed the erosion of <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory materials</a></i></b> up, resulting in increased consumption of<b><i> <a href="http://www.yilongrefractory.com/">refractory</a></i></b> materials.<br />
<br />
Article source:<br />
<b><a href="http://www.yilongrefractory.com/news/Factors%20affecting%20service%20life%20of%20converter.html">http://www.yilongrefractory.com/news/Factors%20affecting%20service%20life%20of%20converter.html</a></b><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-63027566938757755252017-11-02T16:48:00.002+08:002017-11-02T16:48:29.574+08:00How to extend the life of refractory materials<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="refractory materials" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEjJypRxtym2n3UvuOHIAYhB_Gtq6kXbQcvavmtl3PycGSzppaBL8trorcbaPK8UzB77mQamS3wYg6iiaIUYYPGgXfpb9gAJwMSt1MSwFzFJKQI9X08g8XyXoaicTdvGtO6CGgChMqGX0ovY/s320/1.+Magnesia+Carbon+Brick.jpg" title="refractory materials" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/">refractory materials</a></td></tr>
</tbody></table>
How to extend the life of <a data-cke-saved-href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20"><em><strong>refractory materials</strong></em></a>. Generally divided into kiln kiln is divided into four bands, namely, decomposition zone, transition zone, firing zone and cooling zone. Four belt, firing with kiln lining the most critical, at home and abroad in the pre-decomposition kiln burning with the main use of alkaline <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServlet?id=1" href="http://www.yilongrefractory.com/ProductServlet?id=1"><em><strong>refractory brick</strong></em></a>.<br />
Thermal, mechanical and chemical factors contribute to the stress in the kiln lining and cause damage. With the kiln, operation and kiln lining in the kiln position of the different factors of the damage is also different. Which decisive role is the flame, kiln and kiln body deformation, they make the kiln bearing a variety of different stress.<br />
For alkaline tiles, there are eight kinds of destructive factors, namely clinker melt infiltration, agglomeration of volatile components, reduction or reduction - oxidation, overheating, thermal shock, thermal fatigue, extrusion and grinding. However, these eight factors have different effects on the damage of different refractory brick lining in kiln, and the mechanism of damage to alkaline brick is described in this paper.<br />
1, clinker melt infiltration:<br />
Clinker melt mainly from the kiln and fuel, infiltration phase is mainly C2S, C4AF. The infiltration of C2S and C4AF in the metamorphic layer strongly dissolves magnesia and chrome ore in <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=1" href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=1"><em><strong>magnesia carbon bricks</strong></em></a>, precipitates secondary silicates such as CMS and magnesium rose pyroxene (C3MS2), and sometimes even precipitates potassium Stone; and the melt will be filled with brick lining pores, so that part of the brick layer of dense and embrittlement; combined with thermal stress and mechanical stress dual role, resulting in easy cracking refractory brick peeling. Due to C2S, C4AF above 550 ℃ began to form, and pre-decomposition kiln into the kiln material temperature has reached 800 ℃ ~ 860 ℃, so clinker melt penetration throughout the pre-decomposition kiln, the clinker melt on the pre-decomposition Kiln lining with a certain infiltration into the erosion effect.<br />
2, the condensation of volatile components:<br />
Pre-decomposition kiln, alkaline sulphate and chloride and other components volatile agglomeration, repeated circulation, resulting in the accumulation of these components in raw materials. By the production practice, the R2O, SO3 and CI- contents of the raw material in the warmest preheater of the kiln are often increased to 5 times, 3 to 5 times and 80 to 100 times respectively higher than that of the raw material. When the hot material enters the third part of the kiln cylinder (800 ° C to 1200 ° C), the volatile components in the material will aggregate in all the brick and brick layers, And the erosion of the adjacent components other than magnesite, resulting in brick thermal penetration stability of the infiltration layer is significantly reduced, the formation of expansion of potassium nepheline, garnet, the refractory brick lime damage, and thermal - mechanical stress Under the combined action of peeling off. The more the depth of the kiln lining is affected by the alkali salt, Selection.<br />
3, reduction or reduction - oxidation reaction:<br />
When the thermal system in the kiln is unstable, it is easy to produce the reduction flame or the incomplete combustion, so that the Fe3 + reduction or Fe2 + in the magnesia-chrome brick shrinks, and the migration and diffusion of Fe2 + in the magnesite crystal is stronger than Fe3 + More, which further exacerbated the volume shrinkage effect, so that the brick hole, the structure weakened, the intensity decreased. At the same time, the reduction of the kiln gas and the alternating atmosphere of the oxidation of the shrinkage and expansion of the volume effect occurs repeatedly, the brick will produce chemical fatigue. This process mainly occurs in the absence of kiln protection of magnesium chrome brick.<br />
4, overheating:<br />
When the kiln heat load is too high, so that the brick surface for a long time to lose the protection of the kiln, the hot surface layer of the matrix at high temperature melting and moving to the cold layer direction, leaving the brick lining layer of dense, hot surface layer is loose Porous (generally easy to occur in the firing area of the firing zone), which is not resistant to abrasion, shock, vibration and thermal fatigue, easy to damage.<br />
5, thermal shock:<br />
When the kiln is not working properly or kiln leather is unstable, the alkaline tiles are susceptible to thermal shock. Kiln of the sudden collapse of the brick surface temperature caused by a sudden surge (or even up to thousands of degrees), leaving the brick to produce a lot of thermal stress. In addition, the frequent opening and closing of the kiln to produce alternating alternating heat within the brick. When the thermal stress, once beyond the structural strength of the brick lining, the brick suddenly cracks, and along the structure of the weakening of the Department continue to deepen the deepening, and finally the brick fragmentation. When the kiln skin falls, the broken brick in the hot surface layer is taken to keep the brick from damage. The thermal shock phenomenon can easily occur in the transition zone near the kiln.<br />
6, thermal fatigue:<br />
In the kiln operation, when the brick lining is not in the material layer, the surface temperature is lowered, and when the brick lining is exposed to the flame, the surface temperature is increased. Kiln each turn a week, brick lining surface temperature rise and fall range of up to 150 ℃ ~ 230 ℃, the impact of depth 15mm ~ 20mm. Such as pre-decomposition kiln speed of 3r / min, this periodic temperature rise and fall of up to 130,000 times per month. This repeated temperature rise and fall causes the thermal fatigue of the surface layer of the alkaline brick to accelerate the peeling of the brick.<br />
7, squeeze:<br />
Rotary kiln operation, the kiln <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=21" href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=21"><em><strong>refractory lining material</strong></em></a> by the pressure, tension, torque and shear mechanical stress, such as the combined effect. Among them, the rotation of the kiln, the oval of the kiln and the kiln fall, the bricks are subjected to the dynamic load; the weight of the refractory brick and the kiln and the thermal expansion of the brick itself make the brick bear the static load. In addition, between the lining brick and the kiln body, the relative movement between the brick lining and the brick lining, and the welds on the retaining ring and the kiln body, will cause the brick lining to withstand various mechanical stresses. When all these stresses exceed the structural strength of the brick, the brick is cracked. This phenomenon occurs in the kiln lining of the precalciner kiln.<br />
8, wear:<br />
Pre-decomposition kiln kiln discharge area without kiln leather protection, and clinker and large kiln leather and hard, will be on the part of the brick lining, resulting in more serious impact and abrasion damage.<br />
In short, the impact of kiln lining consumption of more factors, but also more complex, and only continue to explore, the use of new technologies, new materials, improve the operation and management level, in order to achieve both reduce consumption, but also the kiln system balanced and stable operation.<br />
More refractory products:<br />
<a data-cke-saved-href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20"><em><strong>http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</strong></em></a><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-5769133081828623832017-11-02T16:20:00.002+08:002017-11-02T16:20:31.457+08:00Principle of Selection of Refractories for Cement Kiln<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="refractory material" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEiQiOKpqUslq21CklAZI9R_vJ0t-jX8TYGZtf8SEo4tLTgYO8sQeGptLQ4cVsJALcgAoK4BG1XCW7teyRL8cyOLrjSo4ihQeyRAEoernuqVc6mxGSf0am0pGg-lmvJ0zFfx0AudDDxjWcIn/s320/22.+Sillimanite+Brick%252C+High+Alumina+Brick%252C+Fireclay+Brick.jpg" title="refractory material" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><em style="font-size: medium; text-align: start;"><strong><a href="http://www.yilongrefractory.com/">refractory material</a></strong></em></td></tr>
</tbody></table>
Preheat zone and decomposition zone<br />
The temperature of these two places is relatively low, <a data-cke-saved-href="http://www.yilongrefractory.com/" href="http://www.yilongrefractory.com/"><em><strong>refractory material</strong></em></a> requiring brick lining of the thermal conductivity is small, good wear resistance, in this area from raw materials, fuel sulfuric acid base and chlorinated alkali began to evaporate, in the kiln condensation and enrichment, and infiltration brick internal. Ordinary clay brick and alkali reaction to form kaolinite and garnet, so that the brick surface crisp, brick body expansion caused by cracking peeling. And containing Al2O3 25% ~ 28% and SiO2 65% ~ 70% of the alkali-resistant or alkali-resistant insulation brick at a certain temperature and alkali reaction, the brick surface immediately formed a layer of high viscosity glaze layer, to prevent the Peeling, but this brick can not resist the use of more than 1200 ℃ temperature. So the preheating zone is generally combined with high alumina <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServlet?id=1" href="http://www.yilongrefractory.com/ProductServlet?id=1"><em><strong>refractory bricks</strong></em></a>, anti-peeling <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=85" href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=85"><em><strong>high alumina bricks</strong></em></a> or resistant to alkali brick.<br />
Decomposition with the general use of anti-peeling good high alumina brick, silicon brick in the performance is better than the anti-peeling good high alumina brick, life than peeling off the high alumina brick about twice as high, but the price is higher, kiln The tail feed should be made of anti-crusted <em><strong><a data-cke-saved-href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=34" href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=34">silicon carbide</a></strong></em> castable.<br />
Transition zone and firing zone<br />
Transition zone kiln leather is unstable, require kiln lining resistance to climate change ability, good thermal shock resistance, thermal conductivity is small, wear. Foreign recommended magnesium aluminum spinel brick, but the thermal conductivity of the brick, the cylinder temperature is high, the relative heat consumption is large, is not conducive to reducing energy consumption. Domestic silicon Mo brick thermal conductivity is small, wear, its performance to a certain extent, comparable with imported materials.<br />
Burning zone with high temperature, intense chemical reaction, requiring brick lining anti-clinker erosion, anti-SO3, CO2 capacity. Foreign generally use magnesium aluminum spinel brick, but the brick hanging kiln skin is more difficult, and dolomite brick thermal shock resistance is not good, easy to hydrate; foreign magnesium iron spinel brick in the hanging kiln skin effect is better , But the cost is too high. The use of new low-chromium perovskite composite spinel brick use is better.<br />
Cooling belt and kiln mouth<br />
Cooling zone and kiln temperature as high as 1400 ℃ or so, the temperature fluctuations, clinker grinding and air erosion are very serious. Requirements of brick lining of the thermal conductivity is small, wear resistance, thermal shock resistance; good thermal shock resistance of alkaline bricks, such as spinel brick or high alumina brick for cooling zone. Foreign generally recommended the use of spinel brick, but the spinel brick thermal conductivity, and wear resistance is not good. Most of the domestic use in recent years, silicon-resistant brick and anti-peeling good wear-resistant brick.<br />
Kiln parts of the use of good resistance to thermal shock castable. Such as: wear-resistant heat-resistant high-alumina brick or steel fiber toughened castables and low-cement high-alumina <a data-cke-saved-href="http://www.yilongrefractory.com/ProductServlet?id=2" href="http://www.yilongrefractory.com/ProductServlet?id=2"><em><strong>refractory castable</strong></em></a>, but the kiln temperature is very high in the large kiln is the use of ordinary, or steel fiber toughening Of the corundum castable.<br />
More refractory products:<br />
<a data-cke-saved-href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20"><em><strong>http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</strong></em></a><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-61915731031067135142017-10-30T13:26:00.001+08:002017-10-30T13:26:17.063+08:00Refractory materials for coke ovens<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/"><img alt="Refractory materials" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEi817JaGPMBHab4ZimujqRSF2EBrmX-b9eEFzmaAqeiZ0pvZayzs2rBRPRlSk4M5WArK-TPZGxYAbxhYaPtU6UZ-tzE-gspdd7tjTv_qGODllKFshRC3tup-dJURafbzJyBiXSIL7vqxCUt/s320/20.+Silica+Brick.jpg" title="Refractory materials" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/">Refractory materials</a></td></tr>
</tbody></table>
Coke oven is the technical equipment of coking plant, is a complex and continuous production of thermal equipment, mainly by the combustion chamber, carbonization room, regenerative, roof, chute, small flue and other components. Its purpose is in the isolated air conditions, the coal heated to 950 ~ 1100 ℃, after dry distillation to obtain coke and other by-products.<br />
At present, the life of a coke oven is generally 25 to 30 years, the use of refractories mainly silica brick, <a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=13"><b><i>clay brick</i></b></a>, high alumina <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1">refractory bricks</a></i></b>. The environmental conditions of the various parts of the coke oven and the requirements for refractory materials are as follows:<br />
Carbonization chamber and partition wall of combustion chamber<br />
The partition wall acts to heat the heat and isolate the furnace gas and support the load. Coke coking temperature is generally 950 ~ 1050 ℃, in order to ensure coking, coke oven wall carbonization chamber side of the surface temperature should be heated to 1100 ~ 1450 ℃; carbonization chamber side of the wall to be thrusting wear; due to coal dry distillation, coking The process in the isolated air conditions, the requirements of the wall air tightness, high temperature airtight, does not occur shrinkage deformation, product shape regular, accurate size to ensure that the small cracks and not cause cracks in the cracks; carbonization chamber in the coking process There is water discharge, the combustion of indoor combustion products contain a small amount of water, and because of coal salt chemical erosion and gas decomposition and carbon deposition, may damage the walls of the organization and performance, strength decreased.<br />
Based on the above characteristics, carbonization chamber and combustion chamber with <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory materials</a></i></b>, the world's coke oven almost all use silicon brick. Silica brick compared with other refractories, in the range of 700 ~ 1450 ℃ within the product changes and thermal conductivity of the small changes in its high temperature strength is high, the load softening temperature and its similarity (1620 ~ 1660 ℃), wear resistance, It is not easy to hydrate. With the large-scale coke oven and strengthen the production needs, can also be used thermal conductivity, volume stability, high temperature strength are high <b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=34">silicon carbide</a></i></b> refractories. But the price is expensive, in the oxidative atmosphere easily oxidized damage, so the curtain wall is rarely used. And the incorporation of metal oxide high-density high thermal conductivity of silicon brick, wall thickness can be reduced, the intensity of heat transfer, improve the productivity of coke oven, but also improve the furnace life.<br />
<br />
More refractories:<br />
<b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</a></b><br />
E-mail:sales8@chinaelong.com<br />
<div>
<br /></div>
cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-30337646521243538862017-10-30T13:01:00.002+08:002017-10-30T17:24:44.953+08:00Refractory materials for iron and steel smelting<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20"><img alt="Refractory materials" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEjSWieLeUu0YHi4BJ4xqQSSBjPE9sSwLu-3748DWuflGEsgQMQHGiSYptHWkY1PprWdnpcnn47xJqwltW6MTSTfH3o3IEmfBQktRz6VnkKx5p4_exaDkFlG28fESABBF4lljrg4Xo-ys8EI/s320/title.jpg" title="Refractory materials" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">Refractory materials</a></td></tr>
</tbody></table>
Blast <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">furnace refractories</a></i></b>:<br />
The development of blast furnace ceramic cups is becoming more and more common, but the need for high corrosion resistance refractory applications to ensure the extension of its service life. In addition to changes in design, <b><i><a href="http://www.yilongrefractory.com/">refractory material</a></i></b> also has a great change, such as micro-porous carbon <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1">refractory brick</a></i></b> instead of the past, ordinary carbon block to reduce the penetration of molten iron. Used clay refractory bricks as raw materials can better meet the requirements of the use of iron mouth guns. The use of grouting method to repair the blast furnace backing can effectively prevent the erosion of the hot air flow, thereby extending the life of blast furnace lining.<br />
Refractory for converter:<br />
In the aspect of converter steelmaking, a water cooling technology and suspension system are respectively applied in the upper cone and lower barrel parts of the converter shell, thereby reducing the deformation of the converter furnace, prolonging the life of the converter lining and improving the converter productivity. The application of these new technologies has had a certain impact on the use of refractories. So that the converter furnace age increased to an average of 4000 furnace or more, combined with the spray, high lime and dolomite applications and slag splashing furnace technology applications, furnace age more than 10,000 times is not a problem. It is worth the attention of <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">refractory producers</a></i></b> to the direction of development.<br />
Continuous submerged nozzle:<br />
Due to the development of the continuous casting system, the tundish has changed from the past transit station to the present metallurgical container which affects the quality of cast steel and improves the productivity of cast steel. Therefore, many functional materials are gradually used in tundish, such as slag weir, impact plate, filter, blowing argon breathable plug and so on.<br />
Immersion nozzle as an important function of continuous casting refractory material, the research carried out mainly in two aspects, one is to improve the slag line parts of the anti-erosion, the second is to reduce the wall of Al2O3 adhesion. The measures to increase the ZrO2 content to 88% and to optimize the particle size distribution can reduce the thermal expansion and porosity of the product and improve the density to improve the slag resistance.<br />
In addition, we should pay close attention to the technological progress of the user industry, such as the recent years of the emergence of direct reduction of iron, and DC arc furnace steel and other new technology on the new requirements of refractories.<br />
<br />
More refractories:<br />
<b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</a></b><br />
E-mail:sales8@chinaelong.com<br />
<div>
<br /></div>
cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com1tag:blogger.com,1999:blog-3569575769022435283.post-15713826118790273552017-10-23T16:52:00.003+08:002017-10-23T16:52:56.568+08:00Furnace with the overall refractory<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/" target="_blank"><img alt="Furnace with the overall refractory" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEgOPhAwngYsEHSidu7jrOsx2QTL12luAFNnLv9m9JztREZMcxxVnyx1qtYKV7yNnacedUyZsbhWFPs3gQlnZsFE7QKMqjs7KsoNd3N1F4yekXWSUXYlYob2zWR9vznQxR56Tb8keLCFt9I_/s320/22.+Sillimanite+Brick%252C+High+Alumina+Brick%252C+Fireclay+Brick.jpg" title="Furnace with the overall refractory" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/" target="_blank">Furnace with the overall refractory</a></td></tr>
</tbody></table>
Rolling furnace is the main business of iron and steel enterprises thermal equipment, its performance directly affect the performance of the enterprise's production and economic benefits, for the majority of thermal workers to improve the performance of the furnace and operating conditions, reduce energy consumption, improve Furnace life, extended overhaul cycle, gallbladder, and achieved encouraging results. In recent years with the mechanical and electrical, <b><i><a href="http://www.yilongrefractory.com/" target="_blank">refractory materials</a></i></b> and other new technologies and materials continue to develop, there have been different design of the regenerative heating furnace, the technical indicators compared with the traditional heating furnace has greatly improved. In the case of<br />
At present, I am in the provision of complete sets of <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" target="_blank">furnace refractories</a></i></b>, has accumulated a wealth of practical experience, according to the user's actual use requirements, to provide a reasonable combination of <b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" target="_blank">refractory products</a></i></b>, the furnace for comprehensive furnace, supporting the use of lower Cost, improve life.<br />
To provide high quality and efficient products, and constantly develop new products, good after-sales technical services, and users work closely with the new product applications to solve the technical problems, so that the new refractory products have been successfully applied, and create economic benefits for users, we Consistent work policy; also my company's purpose.<br />
Some of the products are listed below:<br />
Gravity castable<br />
In addition to the characteristics of high-performance <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=2" target="_blank">refractory castable</a></i></b>, its outstanding advantages are excellent construction performance, construction without vibration, can automatically flow, degassing and dense, the construction of time-saving, effort , High efficiency, to ensure the integrity of the construction body, uniformity and air tightness, in particular, to adapt to the complex structure, high quality requirements of the site, once available by the user's wide welcome. Series of self-flow castables of the technical indicators:<br />
Chrome corundum platform <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1" target="_blank">refractory brick</a></i></b>, slide brick, brick tiles<br />
The furnace trough and tapping platform mechanical wear serious, the temperature fluctuations, high temperature, slag erosion serious, the use of the conditions are extremely harsh, often because of the material wear and tear was forced to stop production maintenance. Where the use of steel fiber reinforced castables, fused mullite tiles, water-cooled cast iron, etc., although achieved good results, but with the increase in production capacity and maintenance cycle to extend the material on the higher The request.<br />
Platform brick, slide brick, refractory brick tiles with high strength, excellent wear resistance and anti-slag erosion strong, long life (up to 1 to 2 years) and so on.<br />
<br />
More refractory material:<br />
<b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</a></i></b><br />
E-mail:sales8@chinaelong.comcxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-27334596995060066772017-10-23T16:28:00.001+08:002017-10-23T16:33:13.005+08:00Refractory materials for industrial furnaces<table cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><span style="clear: left; margin-bottom: 1em; margin-left: auto; margin-right: auto;"><a href="http://www.yilongrefractory.com/" target="_blank"><img alt="Refractory materials for industrial furnaces" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEgHwntNXtGTkcR23UaCEjfpUzyFdahc_HuDr6wtnmbQDtOY2cd8icRie360A-k7bSJhmSc8xQ6MMcmGDw2J56CPsoHLRUy-WeFBzq4e9sBWIfCZHdmPJbhl-I0Wu_vWdLadGT4FVNIo_87D/s320/1.+Magnesia+Carbon+Brick.jpg" title="Refractory materials for industrial furnaces" width="320" /></a></span></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/" target="_blank">Refractory materials for industrial furnaces</a></td></tr>
</tbody></table>
<a href="http://www.yilongrefractory.com/" target="_blank"><b><i>Refractory materials</i></b></a> for industrial furnaces:<br />
High-strength lightweight clay <b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=85" target="_blank">high alumina brick</a></i></b>, high-aluminum foam brick, poly light brick, light <b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=1&id=15" target="_blank">mullite insulation brick</a></i></b>, heavy carburizing <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1" target="_blank">refractory brick</a></i></b>, diatomaceous earth insulation brick, pearlite refractory bricks. All kinds of pit furnace, box furnace, carburizing furnace, trolley furnace, vibration furnace, steel chain plate furnace, mesh belt furnace, crucible furnace, push burning furnace, vacuum furnace, salt bath furnace with light, Heavy standard fire bricks, shaped bricks. Electric corundum furnace tube, silicon carbide furnace tube, high alumina furnace tube.<br />
Electric radiant tube with corundum, high aluminum insulator, plug cover clip.<br />
Electric furnace furnace with corundum silicon carbide brick, radiant furnace floor. Textile machinery singeing machine with a variety of specifications of <b><i><a href="http://www.yilongrefractory.com/ProductServletOne?id1=2&id=34" target="_blank">silicon carbide</a></i></b> fire bricks, honeycomb panels, masonry with a variety of high temperature adhesives.<br />
Fire mud, anti-carburized mud, aluminum silicate fiber cotton, aluminum silicate fiber felt, aluminum silicate fiber board.<br />
<br />
More refractory material:<br />
<b><i><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</a></i></b><br />
E-mail:<a href="mailto:sales8@chinaelong.com"><b>sales8@chinaelong.com</b></a>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-57686473075225252962017-10-17T12:44:00.000+08:002017-10-17T12:44:59.491+08:00Characteristic Refractory Material Mud Mixing Method<span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">Characteristics of </span><a href="http://www.yilongrefractory.com/" style="background-color: white; box-sizing: border-box; color: #3498db; font-family: "Open Sans"; font-size: 16px; text-align: justify; text-decoration-line: none;"><em style="box-sizing: border-box;"><span style="box-sizing: border-box; font-weight: 700;">refractory material</span></em></a><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;"> mud mixture method is to produce special </span><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" style="background-color: white; box-sizing: border-box; color: #3498db; font-family: "Open Sans"; font-size: 16px; text-align: justify; text-decoration-line: none;"><em style="box-sizing: border-box;"><span style="box-sizing: border-box; font-weight: 700;">refractory products</span></em></a><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">, in particular the use of gypsum injection molding, casting and injection molding molding of the mud slurry f operation method is the ingredients of various </span><a href="http://www.yilongrefractory.com/ProductServlet?id=6" style="background-color: white; box-sizing: border-box; color: #3498db; font-family: "Open Sans"; font-size: 16px; text-align: justify; text-decoration-line: none;"><em style="box-sizing: border-box;"><span style="box-sizing: border-box; font-weight: 700;">refractory raw materials</span></em></a><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">, enhancers, Suspending agent, admixture and 30 ~ 40% of the clean water, while adding a wear-resistant lining in the ball mill (mixing mill), after a certain period of mixing fine grinding, made for the production of mud slurry. In the process of making mud, according to the characteristics of materials and mud pouring their own requirements, to control the density and pH of the mud.</span><br style="background-color: white; box-sizing: border-box; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;" /><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">Mud mixing method used by the main equipment are ball mill, air compressor, wet iron, mud pump, vacuum degasser and so on.</span><br style="background-color: white; box-sizing: border-box; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;" /><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">Paraffin and resin-based binder, at room temperature for the solid </span><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20" style="background-color: white; box-sizing: border-box; color: #3498db; font-family: "Open Sans"; font-size: 16px; text-align: justify; text-decoration-line: none;"><em style="box-sizing: border-box;"><span style="box-sizing: border-box; font-weight: 700;">refractory materials</span></em></a><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;"> (or into a sticky), at room temperature, especially law mixture, must be used to increase the method of heating.</span><br style="background-color: white; box-sizing: border-box; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;" /><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">The use of hot casting process, the use of paraffin as a binder. Due to the melting point of paraffin in the 60-80 <€, in the first paraffin heated to 100T or more and have good mobility, and then the fine powder raw materials added to the liquid paraffin, the mixing after mixing, made of slurry Wax cake for hot die casting.</span><br style="background-color: white; box-sizing: border-box; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;" /><span style="background-color: white; color: #606569; font-family: "Open Sans"; font-size: 16px; text-align: justify;">The main mixing equipment for heating the mixture is a heated mixing mixer.</span>cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0tag:blogger.com,1999:blog-3569575769022435283.post-13301020908055232662017-08-28T16:34:00.002+08:002017-08-28T16:34:38.951+08:00The difference between insulation material and refractory material<table align="center" cellpadding="0" cellspacing="0" class="tr-caption-container" style="float: left; margin-right: 1em; text-align: left;"><tbody>
<tr><td style="text-align: center;"><a href="http://www.yilongrefractory.com/" target="_blank"><img alt="refractory material" border="0" data-original-height="500" data-original-width="500" height="320" src="https://blogger.googleusercontent.com/img/b/R29vZ2xl/AVvXsEhAB4YpVt9AZqpHmvnEJwFsE-1mWOapJ-77Rre4A2TqKD0Fp145Fyba-pWdKIcMPBlMCdzK4kZRRaJY_GgGKMR7lh6D4E03F-jC5jKZF-ODc_t-RfG0Aa9kXN8vOw7HaDor9-x_D6iMW9Uj/s320/16.+High+Alumina+EPS+insulating+Firebrick.jpg" style="margin-left: auto; margin-right: auto;" title="refractory material" width="320" /></a></td></tr>
<tr><td class="tr-caption" style="text-align: center;"><a href="http://www.yilongrefractory.com/" target="_blank">refractory material</a></td></tr>
</tbody></table>
<br />
There are many kinds of <a href="http://www.yilongrefractory.com/ProductServlet?id=5" target="_blank"><em><strong>insulation products</strong></em></a>, including foam, mineral cotton products, foam glass, expanded perlite insulation products, EPS powder EPS insulation film, mineral spray cotton, foam cement insulation products. Selection of insulating materials in the construction of the common types of applications and design selection should be consistent with GB / T 17369-1998 "building insulation materials, application types and basic requirements" requirement.<br />
In addition to the material should consider the thermal conductivity of the material, but also should consider the material of water absorption, combustion performance, strength and other indicators. The performance characteristics of different insulation materials see the corresponding classification guide.<br />
<b><i><a href="http://www.yilongrefractory.com/" target="_blank">Refractory material</a></i></b> refractoriness of not less than 1580 ℃ of a class of inorganic non - metallic materials. Refractory degree refers to the refractory cone specimen in the absence of load conditions, resistance to high temperature effect without softening the melting of the Celsius temperature. <b><i><a href="http://www.yilongrefractory.com/" target="_blank">Refractory materials</a></i></b> are widely used in the metallurgical, chemical, petroleum, machinery manufacturing, silicate, power and other industrial fields, the largest in the metallurgical industry, accounting for 50% of the total output of 60%.<br />
Frequently used special materials are AZS <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1" target="_blank">refractory brick</a></i></b>, corundum brick, directly combined with magnesia-chrome brick, silicon carbide brick, silicon nitride combined with silicon carbide brick, nitride, silicide, sulfide, boride, carbide and other non-oxide refractories ; Calcium oxide, chromium oxide, alumina, magnesium oxide, beryllium oxide and other refractories. Frequently used insulation refractory abrasive<br />
Refractory materials are diatomite products, asbestos products, thermal panels and so on.<br />
<br />
Insulation material is used for building envelope or thermal equipment, the heat transfer of the material or material complex, including both insulation materials, including cold materials. <b><i><a href="http://www.yilongrefractory.com/ProductServlet?id=1" target="_blank">Insulation brick</a></i></b> on the one hand to meet the building space or thermal equipment, the thermal environment, on the other hand also saves energy. Therefore, some countries will be adiabatic materials as coal, oil, natural gas, nuclear energy after the "fifth largest energy." A material with a strong resistance to heat flow. Mainly used for housing construction of the wall, roof or industrial pipes, furnaces and other insulation and insulation. According to the principle of insulation is divided into:<br />
① porous material. The gas with a small thermal conductivity is filled with adiabatic pores. Generally the air is the thermal resistance medium, mainly the fibrous aggregation organization and the porous structure material. Foam plastic insulation is better, followed by mineral fibers (such as asbestos), expanded perlite and porous concrete, foam glass.<br />
② Reflective material. Such as aluminum foil can rely on thermal reflection to reduce radiation heat transfer, a few layers of aluminum foil or paper with a thin layer of composite structure, can also increase the thermal resistance. Insulation materials are often used in the form of loose materials, coils, plates and prefabricated blocks for the insulation and insulation of roofs, facades and floors of buildings. Can be directly masonry (such as aerated concrete) or on the roof and envelope for the core material, but also paved into the ground insulation layer. Fiber or granular insulation material can be filled in the wall, can also be sprayed on the wall, both adiabatic, sound absorption, decoration and fire and other effects.<br />
<br />
More refractory material:<br />
<b><a href="http://www.yilongrefractory.com/AllProductServlet?id=1&number=20">http://www.yilongrefractory.com/AllProductServlet?id=1&number=20</a></b><br />
E-mail:sales8@chinaelong.com<br />
<br />cxrefractoryhttp://www.blogger.com/profile/05981944982062373022noreply@blogger.com0