How to recycle refractories?
In a word: Recycle the refractory materials by decomposing them.
The type of refractory materials used in a furnace differs by the position. All kinds of used refractories mixed together make it hard to keep good quality, so it is necessary to classify refractories before reusing them. They can be classified by magnesia, alumina, carbon-based, non-carbon-based.
In addition, for the dissimilar materials or iron mixed in, we can use some ways to pick them out, such as the method of magnetic separation. First, the used refractory materials should be crushed to
400mm, and then reduce to smaller than 20mm after impacting, compression or
snipping, so as to be easy used.
For the refractories mixed with iron, we can use the way of electromagnetic separation, on the effect of magnetic strength higher than 12000 GS, making the content of iron in the used refractories with the size of 5~
less than 2%. While reusing the slit after crushing and after removal of iron
powder as raw materials, we should classify them by particle size. The classification
is generally done by using some metal mesh sieves, put the large mesh screen in
the above and the small mesh screen under the large ones, keep continuously
screening. In the process of crushing, grinding and classification, we should notice
that not let the dust spread, sealing the device and recycling refractories in duster. The left
dust also can be added to raw materials of landscape bricks.
Changxing Refractory,Refractory Brick,Castable,Ladle Nozzle,Calcium Silicate,Silicon Carbide: Advantages of covering agent
Changxing Refractory,Refractory Brick,Castable,Ladle Nozzle,Calcium Silicate,Silicon Carbide: Advantages of covering agent : covering agent ...
covering agent 1, Insulation covering agent is made of low thermal conductivity material composition, such as: expanded perlite, expand...
20th Century 50--70 years, China's steel plants mainly used aluminosilicate refractory materials , including clay, alumina brick and ...
blast furnace refractory lining material 1.Temperature. The damaged performance of high temperature to fire brick: (1)Erosion. When t...