Analysis on firing method of mullite refractory brick

Mullite bricks are sintered mullite bricks and fused mullite bricks.
Mullite Insulating Firebrick refractoriness higher, up to 1790 ℃ or more. The softening start temperature of the load is 1600 to 1700 ° C. Room temperature compressive strength of 70 ~ 260MPa. Thermal shock resistance is good.

Mullite bricks are sintered mullite refractory brick and fused mullite bricks. Sintered mullite brick to bauxite clinker as the main raw material, adding a small amount of clay or bauxite as binder, by molding, firing and made. Fused mullite bricks to high bauxite, industrial alumina and refractory clay as raw materials, by adding charcoal or coke fine particles as reducing agent, forming after the use of reduced melting method to manufacture. The fused mullite is more crystalline than the sintered mullite and has a better thermal shock resistance than the sintered product. Their high temperature properties depend mainly on the alumina content and the homogeneity of the mullite phase with the glass distribution. Mainly used for hot stove top, blast furnace and the bottom of the furnace, glass furnace regenerator, ceramic sintering kiln, oil cracking system, such as dead angle lining.