Application of magnesia carbon brick in Converter Lining

magnesia carbon brick
Changxing Refractory is able to manufacture magnesia carbon brick for every ladle, EAF, and BOF. We will design you a well-balanced lining, providing optimal performance at the lowest possible cost. Our magnesia-carbon brick is made from more than 98% electrically fused magnesite, high purity graphite and metallic antioxidants as needed. Size and specification can be tailored according to furnace type. 
In the smelting process, the use of various parts of the converter conditions, damage is different, for different conditions of use of the various parts of the converter, the masonry refractories are not the same.
(1) furnace mouth: As the furnace temperature changes drastically, slag and high temperature exhaust scouring more powerful, and in the removal of scrap and feeding, the furnace was hit, so the furnace for the refractory material must have a high resistance Thermal shock resistance and slag resistance, to resistance to slag and high temperature exhaust scour, and not easy to hang steel and easy to clean.
(2) furnace cap: the furnace cap is the more serious parts of the slag corrosion, but also by the temperature changes, as well as the oxidation of carbon and dust, such as the role of scouring, so the need for strong slag resistance and thermal shock resistance magnesia carbon brick.
(3) Filling side: The splashing of slag and molten steel is easy to cause chemical erosion, abrasion, erosion, and charging on the charging side. It is also affected by the direct impact and erosion of scrap and molten iron Serious mechanical damage, so the requirements of MgO-C bricks in addition to a high slag resistance and a high high temperature strength, but also must have a very good thermal shock resistance, usually by adding antioxidant high-strength magnesia carbon brick.
(4) the steel side: the steel side of the basic damage from the mechanical damage when the thermal shock is also smaller, but by the tapping of molten steel when the thermal shock and erosion, damage faster than the loading side of the small When the same material as the charging side is used, in order to maintain the equilibrium life of the converter charge, we use masonry with a thickness in the form of a thin side.
(5) slag line parts: slag line is the long-term contact with the slag and slag corrosion serious parts, in the tapping side, with the slag position with the tapping time changes, and more obvious. In the slag side, due to the strong impact of the slag erosion and the other effects of the abdomen caused by the abdomen in the process of blowing, the damage is serious, so we need to masonry with good slag resistance of magnesia carbon refractory brick.
(6) trunnion on both sides: both sides of the trunnion in addition to the role of damage when blowing, the surface of the protective layer of the cover, not easy to repair, so the charge material in the carbon easily oxidized, and thus damaged, Excellent slag resistance, high oxidation resistance of high-grade magnesia carbon brick.
(7) hearth and bottom: these parts in the blowing by the severe scouring of molten steel, but compared with other parts of the damage to a more tired, the choice of low carbon content of magnesia carbon brick can also be used tar dolomite brick The When the high-speed blowing and the pool is too shallow, the bottom of the furnace site damage may be serious. In addition, when the use of bottom blowing, these parts of the damage may increase, should be used and the furnace side of the same material.