1.Lift the installed pneumatic vibrator into the forma, put it in the bottom, and then raise it by 50mm. Adjust the distance between the hammer head and the forma. With 30mm as the standard, ensure that the hammer head can effectively contact the inner lining of forma.
2.Turn on the gas valve for 30 seconds at low speed, then vibrate at full speed, and vibrate for 5 to 8 minutes for each 100mm increase until 300mm below the top of the furnace.
3. Furnace Heating Technique of Former Patching Lining
3a) Fully fill small and dense scrap materials into the furnace, and heat up at 100-200 celsius degree per hour.
3b) During melting, raise powers slowly to ensure crucible not break until it is full.
3c) Keep heat preservation for one hour at 1680-1700 celsius degree, detecting temperature once per 20 minutes.
3d) After sintering finished inside furnace, it can start to work.
Article source:
http://www.yilongrefractory.com/news/How%20to%20do%20lining%20construction.html
E-mail:sales8@chinaelong.com
Web: www.yilongrefractory.com E-mail: sales8@chinaelong.com Professional refractory products manufacturer from China since 1978, deals on exploration, whose products have been exported to more than 20 countries. Product portfolio covers shaped and unshaped products, such as fire brick, impact plate, ladle and tundish nozzle, calcium silicate board and pipe, ceramic fiber, slide gate, repair, construction and casting mortar and mixes, etc.
订阅:
博文评论 (Atom)
Refractory Material, Fire Bricks, Refractory Manufacturer, China Refractory - CX Refractories
Refractory Material, Fire Bricks, Refractory Manufacturer, China Refractory - CX Refractories
-
blast furnace refractory lining material 1.Temperature. The damaged performance of high temperature to fire brick: (1)Erosion. When t...
-
Furnace with the overall refractory Rolling furnace is the main business of iron and steel enterprises thermal equipment, its performanc...
-
Company News | Xinmi Changxing Refractory Co.,Ltd
magnesia carbon brick, MgO-C Bricks,
回复删除Ladle magnesia carbon brick takes use of fused magnesia sand, high carbon graphite as raw material, adding proper amount of antioxidants, bonded with phenolic resin,made by high pressure molding. Ladle mgo-c bricks has good erosion resistance and shock resistance. Ladle lining magnesia carbon brick are generally used in furnace lining.
http://www.ruizhirefractory.com/en/product/ladle-magnesia-carbon-brick.html